- 525 Fatigue Behaviour of Friction Stir Welded 1050 and 5083 Aluminium Alloys
この論文をさがす
抄録
Fully reversed axial fatigue tests have been performed in order to investigate fatigue behaviour in friction stir welded (FSW) joints of 1050 and 5083 aluminium alloys. In 5083 FSW joints, fatigue failure occurred in the parent metal away from the weld centre, leading to similar fatigue strength to the parent metal. In 1050 FSW joints, however, fatigue crack initiated near the boundary between thermo-mechanically affected zone and heat affected zone, which resulted in lower fatigue strength of the joint than the parent metal. This was attributed to the local plastic deformation due to the discontinuity of hardness at the boundary.
収録刊行物
-
- M&M材料力学カンファレンス
-
M&M材料力学カンファレンス 2007 (0), 385-386, 2007
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205870789760
-
- NII論文ID
- 110008697003
- 120006341136
-
- NII書誌ID
- AA12322087
-
- ISSN
- 24242845
-
- HANDLE
- 20.500.12099/40086
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- IRDB
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可