PS15 環状切欠試験片を用いたひずみ制御高温クリープ・疲労重量条件下におけるP92鋼のき裂成長寿命の繰返し速度特性(フェロー賞対象ポスターセッション)

• 中川 拓大

  東北大院

• 杉浦 隆次

  東北大

• 横堀 壽光

• 足立 岳志

  石巻専修大

• 松崎 隆

  東北大

• 野中 勇

書誌事項

タイトル別名

• PS15 The Characteristics of Load Frequency on the Crack Growth Life of a Circular Notched Specimen under Strain Control Creep-Fatigue Conditions for P92

抄録

W strengthened 9Cr ferritic heat resistant steel has been applied to boiler materials for the most efficient electric power plant technology and it will be used under the conditions of high temperature creep-fatigue multiplication. In this study, mechanical tests under the conditions of high temperature creep-fatigue multiplication were conducted for W strengthened 9%Cr ferritic heat resistant steels (ASME-Code P92) with various stress holding time conditions. Based on these results, the characteristics of load frequency of crack growth life were investigated by analyzing cycle-dependent and time-dependent mechanisms on the characteristic of load frequency of crack growth life.

収録刊行物

• M&M材料力学カンファレンス

  M&M材料力学カンファレンス 2010 (0), 38-40, 2010

  一般社団法人 日本機械学会

キーワード

• Creep
• Fatigue

詳細情報

• CRID: 1390001205872611712
• NII論文ID: 110008741052
• DOI: 10.1299/jsmemm.2010.38
• ISSN: 24242845
• Web Site: https://www.jstage.jst.go.jp/article/jsmemm/2010/0/2010_38/_pdf
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可