• J111011 Synthesis and tribological property of high density nanodiamond-electroless nickel plating composite

抄録

In this study, nanodiamond (ND)-electroless Ni plating composite coating was synthesized for high wear resistance and low friction. The ND-Ni plating composite coating was prepared from electroless Ni plating solution dispersing diamond nano particle (DNP) on S50C substrate. Heat treatment to increase hardness of electroless Ni plating was conducted in this coating. Tribological properties of the ND-Ni plating composite coating was investigated under three lubricant conditions (no lubrication, water lubrication and 1wt.% DNP dispersion). Under the DNP dispersion, the friction coefficient of ND-Ni plating composite film and Ni plating coating were lower than other conditions. Severe wears after the friction tests were observed on the ND-Ni plating composite coating under no lubrication, however only small protrusion of the composite film tested under the DNP dispersion was worn.

収録刊行物

• 年次大会

  年次大会 2013 (0), _J111011-1-_J111011-4, 2013

  一般社団法人 日本機械学会

キーワード

• Diamond nano particle
• electroless nickel plating

詳細情報

• CRID: 1390001205839935360
• NII論文ID: 110009935377
• DOI: 10.1299/jsmemecj.2013._j111011-1
• ISSN: 24242667
• Web Site: https://www.jstage.jst.go.jp/article/jsmemecj/2013/0/2013__J111011-1/_pdf
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可