J191026 耐紫外線性の向上を目的としたエポキシ/TiO_2ナノコンポジットの試作([J191-02]構造・材料の高度化に向けた宇宙工学と材料力学の展開(2))

• 中村 孝

  北海道大学大学院工学研究院

• 静 宏幸

  北海道大学大学院工学院

• 小熊 博幸

  北海道大学大学院工学研究院

書誌事項

タイトル別名

• J191026 A Trial Production of Epoxy/TiO_2 Nanocomposites to Improve Ultraviolet Light Resistance

抄録

This study carried out a trial production of Epoxy/TiO_2 nancomposites to improve ultraviolet light resistance. Two kinds of TiO_2 particles with a diameter of 30nm and 270nm were dispersed in the epoxy resin and the ultraviolet light resistance was evaluated based on UV irradiation tests, tensile tests, and SEM observations of specimen surfaces and fracture surfaces. As a result, elongation at break of epoxy resin and epoxy/TiO_2(270nm) composite decreased after UV irradiation although that of epoxy/TiO_2(30nm) composite remained unchanged. Epoxy/TiO_2 (30nm) composite likely to suppress the embrittlement of surface layer caused by UV irradiation, and tend to reduce the crack initiations which deteriorate strength properties.

収録刊行物

• 年次大会

  年次大会 2013 (0), _J191026-1-_J191026-3, 2013

  一般社団法人 日本機械学会

キーワード

• High Polymer Materials
• Photodegradation
• Tensile Properties
• Crack Propagation
• Fractography

詳細情報

• CRID: 1390282680818779904
• NII論文ID: 110009935505
• DOI: 10.1299/jsmemecj.2013._j191026-1
• ISSN: 24242667
• Web Site: https://www.jstage.jst.go.jp/article/jsmemecj/2013/0/2013__J191026-1/_pdf
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可