- OS1426 The effect of differential term of stress intensity factor on fatigue crack growth behaviour
抄録
There is a possibility that the crack growth rate of stress corrosion cracking and fatigue crack depend on the value of ∂K/∂a (differential term of stress intensity factor) as well as stress intensity factor K. In this study, the effect of ∂K/∂a on crack growth rate was investigated during the fatigue test. Two types of specimens were prepared. One is CT specimen of which K increases under constant loading. The other is CDCB specimen of which K is constant. The effect of ∂K/∂a was clarified by comparing the CT specimen and CDCB specimen under same stress intensity factor. In addition, ΔK corrections considering ∂K/∂a were conducted for CT specimens. As a result, the crack growth rates in CT specimens were larger than CDCB specimens in the same ΔK. Corrected ΔK considering ∂K/∂a is mostly coincides with the value of the CDCB specimen. From those results, the crack growth rate varied due to the effect of ∂K/∂a in fatigue crack propagation was experimentally clarified. In addition, elimination of the influence of ∂K/∂a is possible by ΔK correction.
収録刊行物
-
- M&M材料力学カンファレンス
-
M&M材料力学カンファレンス 2013 (0), _OS1426-1_-_OS1426-3_, 2013
一般社団法人 日本機械学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282680850482560
-
- NII論文ID
- 110009936745
-
- ISSN
- 24242845
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可