- OS1505 Investigation of Fatigue Crack Behaviour on Dissimilar FSW Joints by Laminography with Synchrotron Radiation
抄録
Microstructure and a fatigue crack propagation path inside a dissimilar friction stir welded plate between A2024 and A6061 aluminum alloys were visualized with synchrotron radiation computed laminography at SPring-8. A fatigue crack propagated in a different direction from the perpendicular to fatigue loading under the influence of the plastic flow pattern in the weld. However, the fatigue crack shape projected onto the loading direction was similar to a half penny shape, and the aspect ratio decreased with increasing fatigue life. There was an interface plane between A2024 and A6061 in the welding zone but the fatigue crack propagation was not affected by the presence of the interface.
収録刊行物
-
- M&M材料力学カンファレンス
-
M&M材料力学カンファレンス 2013 (0), _OS1505-1_-_OS1505-3_, 2013
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205873758336
-
- NII論文ID
- 110009936753
-
- ISSN
- 24242845
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可