- OS1606 A Development of Cyclic Press Method for Nano-structural Refinement of Metal Surface
抄録
In recent studies of very high cycle fatigue, a unique phenomenon of nano-structural refinement has been observed beneath fracture surfaces due to a large number of repeating contacts of themselves over 10^7 cycles. Focusing on this phenomenon, this study proposed a new surface treatment named Cyclic Press Method to refine metal surface without profound plastic deformation. A low cyclic compressive load was given to the surface of Ni-Cr-Mo steel (SNCM439) and Al-Si-Cu die-casting alloy (ACD12) for 5×10^7 cycles. After that, the longitudinal section was processed by FIB and was observed with SIM. As a result, the nanocrystalline structure was clearly formed in the surface layer of both materials. The size of nano-grains and the depth of nano-layer were different between two materials; however, the Cyclic Press Method was shown to be effective in nano-structural refinement of metal surface.
収録刊行物
-
- M&M材料力学カンファレンス
-
M&M材料力学カンファレンス 2012 (0), _OS1606-1_-_OS1606-3_, 2012
一般社団法人 日本機械学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282680848899968
-
- NII論文ID
- 110009937482
-
- ISSN
- 24242845
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可