- OS2110 Effect of ultrasonic shot peening on the fatigue crack initiation and propagationbehavior of stainless cast steel SCS6 for the turbine runner of hydraulic power generation
抄録
This study aimed to examine the effect of ultrasonic shot peening (USP) process on the fatigue strength of stainless cast steel JIS SCS6 for hydraulic turbine runner. Fatigue test was carried out in laboratory air room temperature using the specimens which was treated USP (USP specimen) and was not (Virgin specimen). It was found that the modified layer formed by USP process had high hardness and compressive residual stress. The fatigue strength of USP specimen rose about 60% in comparison with Virgin specimen. The fatigue crack in each type specimen was observed in detail by using plastic replica technique. The fatigue crack initiation life of USP specimen was more extension than that of Virgin specimen. The fatigue crack propagation rate of USP specimen was lower than that of Virgin specimen. The modified layer formed by USP process affects the fatigue crack initiation life and the propagation rate. The two reasons are the factor of the improvement of the fatigue strength by USP process.
収録刊行物
-
- M&M材料力学カンファレンス
-
M&M材料力学カンファレンス 2012 (0), _OS2110-1_-_OS2110-3_, 2012
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205870709760
-
- NII論文ID
- 110009937543
-
- ISSN
- 24242845
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可