抄録

A compatible-symmetric-type bicyrystal model and incompatible-type bicrystal models having inclined grain boundary were employed to conduct crystal plasticity analysis of unidirectional tensile tests, and we investigated changes in patterns of Geometrically Necessary dislocation (GND) bands when nominal strain was 1 %. The results showed that GND bands, where the inclination angle was about 45°, developed from the intersection point of the grain boundary with the upper or bottom edge, and the bands inclination was unalterable independently of angles of the grain boundary inclination. On the other hand, sign of densities of GN dislocations within the bands was changed when the grain boundary inclination was changed from 45° to 46°. This is because the mechanical restraint at the upper and bottom edge and the grain boundary strongly affects formation of GND bands rather than the inclination of grain boundary.

収録刊行物

• M&M材料力学カンファレンス

  M&M材料力学カンファレンス 2014 (0), _OS0113-1_-_OS0113-3_, 2014

  一般社団法人 日本機械学会

キーワード

• Crystal Plasticity Analysis
• GND Bands
• Bicrystal Model

詳細情報

• CRID: 1390001205876088064
• NII論文ID: 110009939440
• DOI: 10.1299/jsmemm.2014._os0113-1_
• ISSN: 24242845
• Web Site: https://www.jstage.jst.go.jp/article/jsmemm/2014/0/2014__OS0113-1_/_pdf
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可