818 キンク損傷がPBO繊維の引張破壊挙動に及ぼす影響(GS4-4 材料力学・計算力学)

• 川野 優希

  富山県立大学大学院工学研究科

• 堀川 教世

  富山県立大学工学部

• 宮島 敏郎

  富山県立大学工学部

• 上野 明

  立命館大学理工学部

• 境田 彰芳

  明石工業高等専門学校

• 森 孝男

  富山県立大学工学部

書誌事項

タイトル別名

• 818 Effect of Kinking Damage on Tensile Fracture Behavior of PBO Fiber

抄録

In this paper, effect of kinking damage on tensile fracture behavior of poly-p-phenylene benzobisoxazole (PBO) fiber was investigated in monofilament tests. Kinking damages was created on surface of virgin fiber by winding bundle fibers to steel rod. Diameter of steel rod was set to 5, 2.5, 1.25 and 0.65 mm. Kinking damage density was defined to evaluate occurrence of kinking damage owing to bundle fiber was wound onto the steel rod. The fracture surface was observed using Scanning Electron Microscope (SEM). It was found that the tensile strength of fiber with kinking damage was well fitted the Weibull distribution function with 2 parameters. The tensile strength of PBO fiber with kinking damage was explained in the concept of the effective volume. It was shown that the crack growth of PBO fiber with kinking damage developed along the kinking damage.

収録刊行物

• 北陸信越支部総会・講演会　講演論文集

  北陸信越支部総会・講演会　講演論文集 2016.53 (0), _818-1_-_818-5_, 2016

  一般社団法人 日本機械学会

キーワード

• High Polymer Materials
• Kinking Damage
• Tensile Strength
• Compressive Strain
• Weibull Distribution

詳細情報

• CRID: 1390282680846140032
• NII論文ID: 110010045720
• DOI: 10.1299/jsmehs.2016.53._818-1_
• ISSN: 24242772
• Web Site: https://www.jstage.jst.go.jp/article/jsmehs/2016.53/0/2016.53__818-1_/_pdf
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可