- OS1201-428 Influence of molten CMAS (CaO-MgO-Al_2O_3-SiO_2) infiltration on the mechanical property of thermal barrier coatings and their delamination behavior
抄録
The importance of TBC (Thermal Barrier Coating) is increasing with development of high performance gas turbine system that can operate at higher temperature. The TBC, which consists of ceramic top coating layer and metallic bond coating layer, deteriorate by the high temperature loading condition. The CMAS (CaO-MgO-Al_2O_3-SiO_2) infiltration into the topcoat is also one of degradation mechanism of TBCs. Delamination of the topcoat with CMAS infiltrated layer was observed in this study. Increasing in elastic modulus of a CMAS infiltrated TBC topcoat was also observed. Thermal stress analysis was conducted in this study. The results indicate that the compressive stress state that can promote a buckling-mode coating delamination developed in the CMAS infiltrated topcoat.
収録刊行物
-
- M&M材料力学カンファレンス
-
M&M材料力学カンファレンス 2015 (0), _OS1201-42-_OS1201-42, 2015
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680852168448
-
- NII論文ID
- 110010053559
-
- ISSN
- 24242845
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可