Amorphous Oxides Prepared from Organometallic Compounds Part2. Structure Evolution in Sodium Borosilicate Gels
この論文をさがす
抄録
Sodium borosilicate gels of compositions similar to that of Vycor(R) glass like 80SiO(2).15B(2)O(3).5Na(2)O (wt%) were prepared from hydrolysis and polycondensation of metal alkoxides under the HCl catalysis. Variation of specific surface area and porosity with temperature indicated that closed pores were opened below 400℃, and collapsed above 450℃ after the porosity reached a maximum value around 450℃. The structural evolution was examined due to IR spectra and a phase separation in the gels was observed. The solubility of the gels into 1N-HCl was studied as a function of the treatment temperature.
収録刊行物
-
- Memoirs of the Faculty of Engineering, Okayama University
-
Memoirs of the Faculty of Engineering, Okayama University 23 (1), 39-48, 1988-11-22
Faculty of Engineering, Okayama University
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390009224557006336
-
- NII論文ID
- 120002307518
-
- NII書誌ID
- AA10699856
-
- ISSN
- 04750071
-
- DOI
- 10.18926/15462
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- IRDB
- CiNii Articles