- Change in Structure of 9Cr-1Mo Steel by Heat-treatment after Cold Working
- レイカン カコウ ゴ ノ ネツ ショリ ニ ヨル 9Cr-1Moコウ ノ ソシキ ヘンカ
この論文をさがす
抄録
The change in structure of 9Cr-1Mo steel caused by heat-treatment after cold working was investigated on the basis of Vickers hardness test, X-ray diffraction, and SEM observation. Many precipitates of chromium carbide were observed in the surface of cold-rolled specimens. By the heat-treatment at 700℃, the growth of grain and precipitate were observed. We measured Vickers hardness, HV, and the half-value width of X-ray diffraction peak for the specimen heat-treated after the cold-rolling. By heat-treatment at 100-200℃, HV slightly increased, but the half-value width was nearly constant. At the heat-treatment temperature at 200-500℃, Vickers hardness, HV, increased slightly, and the half-value width decreased. These phenomena result from the diffusion of interstitial impurities around dislocations. At 500-700℃, both HV and the half-value width decreased. The decrease in HV and the half-value width is caused by recrystallization, that is, large decrease in dislocation density.
収録刊行物
-
- 福井工業大学研究紀要
-
福井工業大学研究紀要 (44), 53-59, 2014-07-11
福井工業大学
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390577763028523904
-
- NII論文ID
- 120005456490
-
- NII書誌ID
- AA12450746
-
- ISSN
- 18844456
-
- NDL書誌ID
- 025593528
-
- データソース種別
-
- JaLC
- IRDB
- NDL
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用可