Evaluation of ductile damage in aluminum single crystal with prior activity of single slip system under tensile loading

DOI 機関リポジトリ PDF 被引用文献1件 参考文献8件

書誌事項

タイトル別名
  • Evaluation of Ductile Damage Progress of Aluminum Single Crystal with Prior Activity of Single Slip System under Tensile Loading by Using Synchrotron White X-Ray

抄録

A ductile damage progress of an aluminum single crystal with the prior activity of the single slip system under tensile loading was verified by a profile analysis using white X-ray obtained in BL28B2 beam line of SPring-8. In this study, the aluminum single crystal of the purity 6N was used as a specimen prepared in I-type geometry for tensile test. A notch was introduced into one side of the center of a parallel part of the specimen by the wire electric discharge machining. White X-ray beam, which has 50 μm in both height and width, was incident into the specimen on the Bragg angle θ of 3 degrees using energy dispersive X-ray diffraction technique. The specimen was deformed by elongation in the direction of 45°to [11 and [11 crystal orientations, respectively, and a diffraction profile of the white X-ray from Al220 plane was analyzed. In profile analysis, an instrumental function was defined in consideration both of a divergence by a slit and a response function peculiar to the energy dispersive method. The Gauss component of integral breadth related to non-uniform strain and the Cauchy component of integral breadth related to crystallite size were determined by eliminating the broadening by the instrumental function from the diffraction profile of white X-ray. As a result, the characteristics of ductile damage progress near the notch of the aluminum single crystal were inspected from the distribution of both non-uniform strain and dislocation density.

収録刊行物

被引用文献 (1)*注記

もっと見る

参考文献 (8)*注記

もっと見る

関連プロジェクト

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ