溶鉄のAl2O3に対する濡れ性におよぼす酸素,温度の影響

• 田中, 泰邦

• 篠崎, 信也

• 向井, 楠宏

書誌事項

タイトル別名

• ヨウテツ ノ Al2O3 ニ タイスル ヌレセイ ニ オヨボス サンソ オンド
• Effects of Oxygen and Temperature on Wettability of Al203 by Molten Iron

抄録

The effects of temperature and oxygen on the wettability of alumina substrates by liquid iron were measured at the temperature range from 1823K to 2023K over the wide range of oxygen concentration up to 0.08mass% by use of the sessile drop method. Obtained results are as follows;(1) Contact angle of liquid iron on alumina substrate decreases with increasing oxygen concentration in liquid iron, but does not change with temperature.(21 Work of adhesion between liquid iron and aulmina substrate decreases with increasing oxygen concentration, but does not change with temperature.(3) Above 0.04mass% of oxygen concentration in liquid iron, contact angle and work of adhesion are kept to bo nearly constant and hercynite (FeO・Al203) was identified at the interface between liquid iron and alumina substrate by X-ray method. It was estimated from work of adhesion and interfacial excess quantity for oxygen that oxygen ion existed at the interface with close-packing.

収録刊行物

• 耐火物

  耐火物 44 (2), 58-64, 1992-02-01

  耐火物技術協会

キーワード

• wettablity
• work of adhesion
• alumina substrate
• sessile drop method
• interfacial excess quantity

詳細情報

• CRID: 1050564288864327552
• NII論文ID: 120005954671
• NII書誌ID: AN00136247
• ISSN: 00398993
• HANDLE: 10228/6001
• NDL書誌ID: 3758322
• Web Site: https://kyutech.repo.nii.ac.jp/records/4781
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I3758322
• 本文言語コード: ja
• 資料種別: journal article
• データソース種別:
  • IRDB
  • NDL
  • CiNii Articles