書誌事項
- タイトル別名
-
- Heat Degradation of Poly(propylene) in Extruding Cycles
- ポリプロピレン ノ セイケイ カコウジ ニ オケル ネツ レッカ
この論文をさがす
抄録
Poly(propylene) samples were reprocessed in multiple cycles by a single-screw extruder. The heat degraded samples reprocessed were characterized by dynamic viscoelasticity and stress-strain measurement.<br>The decrease (Mw/Mw0) in molecular weight of poly(propylene) with reprocessing was expressed by the product (f(n, T)·g(t, T)) of a function of cycles number (n) of extrusion consisting of virgin and degraded samples and a function of time (t) required in extrusion at a given temperature (T). Especially, at a temperature below 190°C, Mw/Mw0 was expressed only by f(n, T). In blend system Mw/Mw0 was expressed by similar relationship, suggesting that the synergy effect of blend on the heat degradation was absent. Young’s modulus (E) and yield stress (σy) obtained from stress-strain curves did not change regardless of the virgin, heat degraded and blend samples.
収録刊行物
-
- 環境資源工学
-
環境資源工学 51 (2), 77-82, 2004
一般社団法人 環境資源工学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282680184820224
-
- NII論文ID
- 130000103638
-
- NII書誌ID
- AA11907992
-
- ISSN
- 13499262
- 13486012
-
- NDL書誌ID
- 6980451
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可