Microwave Heating Behavior of Blast Furnace Slag Bearing High Titanium

• YAN Chen

  Tohoku University

• YOSHIKAWA Noboru

  Graduate School of Environmental Studies, Tohoku University

• TANIGUCHI Shoji

  Graduate School of Environmental Studies, Tohoku University

抄録

Blast furnace (BF) slag in south-western part of China contains large amount of titanium. For the purpose of beneficial utilization of titanium in the slag, microwave (MW) processing of the slag has been proposed. In this study, a fundamental research on heating behavior of the slag by application of 2.45 GHz MW was performed.<br>The slag specimens can be heated in a domestic MW oven at constant input power (0.5 kW) and sudden increase of the temperature is observed after several heating cycles. A phenomenon of so-called thermal runaway (TRW) occurred. A part of the specimen melted, and the XRD analysis indicated that this area became amorphous. Crystallization of the CaTiO₃ phase occurred by MW heating of the melted slag at 600°C.<br>A sintered CaTiO₃ compact was heated by MW much more than the synthetic Chinese slag. The synthetic slag without containing Ti was not heated very well. Permittivity of CaTiO₃ (loss factor) was measured and demonstrated to be much larger than the other oxides in the slag. Therefore, it is concluded that CaTiO₃ phase is responsible for heating of the whole slag.

収録刊行物

• ＩＳＩＪ　Ｉｎｔｅｒｎａｔｉｏｎａｌ

  ＩＳＩＪ　Ｉｎｔｅｒｎａｔｉｏｎａｌ 45 (9), 1232-1237, 2005

  一般社団法人 日本鉄鋼協会

キーワード

• microwave
• blast furnace slag
• titanium
• perovskite
• heating
• crystallization
• permittivity
• Chinese slag

詳細情報

• CRID: 1390282681463520000
• NII論文ID: 130000251175
• DOI: 10.2355/isijinternational.45.1232
• COI: 1:CAS:528:DC%2BD2MXhtVOltbbL
• ISSN: 13475460
• ISSN: 09151559
• Web Site: http://www.jstage.jst.go.jp/article/isijinternational/45/9/45_9_1232/_pdf
• 本文言語コード: en
• データソース種別:
  • JaLC
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可