Electrodeposition Behavior of Zn-Iron-group Metal Alloys from Sulfate and Chloride Baths.
-
- Fukushima Hisaaki
- Faculty of Engineering, Kyushu University
-
- Akiyama Tetsuya
- Faculty of Engineering, Kyushu University
-
- Yano Masaaki
- Graduate School, Kyushu University
-
- Ishikawa Tatsuo
- Graduate School, Kyushu University
-
- Kammel Roland
- Institute of Metallurgy, Technical University of Berlin
抄録
Electrodeposition of Zn-iron-group metal binary alloys, which has been applied in the production of highly corrosion-resistant alloy plated steel sheet, was conducted from sulfate and chloride baths and the alloy deposition behavior was compared between two types of baths. The current density-dependence of alloy composition showed a typical feature of an anomalous codeposition in the sulfate baths. In the chloride baths, the deposition behavior was shifted gradually from an anomalous to a regular type with increasing chloride ion concentration. On the basis of the factors determining the characteristic current density at which Zn deposition began, the alloy deposition behavior was discussed with the particular reference to the effect of catalytic chloride ions for iron-group metal deposition.
収録刊行物
-
- ISIJ International
-
ISIJ International 33 (9), 1009-1015, 1993
一般社団法人 日本鉄鋼協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681430416384
-
- NII論文ID
- 130000781688
-
- COI
- 1:CAS:528:DyaK2cXhsVSqur8%3D
-
- ISSN
- 13475460
- 09151559
- http://id.crossref.org/issn/09151559
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可