- Sintering mechanisms and mechanical properties of Mo2FeB2 based hard alloys.
- Mo2FeB2 ホウカブツケイ コウシツ ゴウキン ノ ショウケツ キコウ ト
この論文をさがす
抄録
The sintering phenomena of Fe-6 wt%B-(0-58) wt%Mo alloys are studied by means of TG-DTA, dilatometric measurements and X-ray diffractometry. In addition, the mechanical properties of the sintered alloys are discussed.<BR>The optimum process-property relations can be summarized as follows:<BR>(1)Highest transverse rupture strength values around 200 kg/mm2 are obtained for the 48 wt%Mo alloy.<BR>(2)The 48 wt%Mo alloy consists of the Mo2FeB2 and a small amount of Fe2B as hard phases and of an Fe binder phase.<BR>(3)The Mo2FeB2 phase is formed in the temperature range 750-1090°C. The liquid phase sintering of the alloy is accomplished by two different liquid phases produced by two different reactions. The first reaction, γ-Fe+Fe2B→L1, occurs in a temperature range 1090-1150°C, this being somewhat lower than expected for the binary Fe-Fe2B system presumably due to the presence of Mo. The second reaction, γ-Fe+Mo2FeB2→L2, occurs above 1150°C.<BR>(4)The optimum sintering temperature lies slightly above the temperature at which the reaction γ-Fe+Mo2FeB2→L2 occurs.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 34 (7), 302-308, 1987
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681283992576
-
- NII論文ID
- 130000813138
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 3158033
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可