- Influences of alloy elements in infiltrant on mechanical properties of copper-alloy infiltrated P/M high speed steels.
- ドウ ヨウシン ショウケツ コウソクド コウ ノ ショ セイシツ ニ オヨボス
この論文をさがす
抄録
Elements in Infiltrant on Mechanical Properties of Copper-alloy Infiltrated P/M High Speed Steels<BR>Mechanical properties of copper-alloy infiltrated M42, T42 P/M high speed steels were studied.The green compacts were sintered in vacuum at 1433, 1443, 1453 K to make skeletons. The skeletons were infiltrated with Cu-Cr, Cu-Co and Cu-Fe-Mn alloy infiltrants in hydrogen or argon at 1423 K for 1.8 ks.The result obtained were summarized as follows.<BR>1)All the infiltrated specimens shrinked.The Cu-Fe-Mn infiltrated M42, T42 P/M high speed steels had the least amount of dimentional change values during infiltration.The Cu-Fe-Mn infiltrated M42, T42 P/M steels had comparatively high hardness, but low strength.<BR>2)Cu-Cr, Cu-Co infiltrated P/M high speed steels showed high strength, especially the P/M M42 steel having a skeleton sintered at 1453 k in vacuum and infiltrated with the Cu-Co alloy infiltrant in hydrogen had 2450 MPa of transverse rupture strength and HRC 48 of hardness as infiltrated.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 37 (2), 214-218, 1990
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206304076416
-
- NII論文ID
- 130000813862
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 3669251
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可