- Effect of size distribution and oxide layer on pressing and sintering of water-atomized SUS 316L stainless steel powders
- ミズ フンム SUS316L ステンレス コウフン ノ アッシュク ショウケツ
この論文をさがす
抄録
Pressing and sintering of SUS. 316L stainless steel powders were studied under various size distribution and amount of surface oxidation.<BR>The results were summarized as follows:<BR>1) Compressibility was higher with mixtures of about 40/60 coarse/-325 mesh powders (permitting some difference in compacting pressure), mainly because of change in shape with particle size.<BR>2) When vacuum-sintered at temperature above 1200°C, -325 mesh size distribution gave maximum sintered density. In other words, the sintering rate was controlled by mixing ratio of fine powders to coarse powders.<BR>3) Oxide layer of stainles steel powder gave poor compressibility, and also-less densification because of delaying effect on mass transport during sintering.<BR>4) Residual oxide layer (inclusion) affected pore-morphology in sintered materials. Therefore, the mecha-nical properties were appreciably deteriorated under higher sintered density with oxygen-content over 0.3 pct.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 23 (1), 11-19, 1976
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681284306432
-
- NII論文ID
- 130000814532
- 10003590383
-
- NII書誌ID
- AN00222724
-
- COI
- 1:CAS:528:DyaE1cXmtVWgtrg%3D
-
- ISSN
- 18809014
- 05328799
- http://id.crossref.org/issn/05328799
-
- NDL書誌ID
- 1697723
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可