- Effect of Porosity on the Tensile Strength of Sintered Compacts (I)
- ショウケツタイ ノ ヒッパリ ツヨサ ト キコウリツ ノ カンケイ 1
この論文をさがす
抄録
The relationship between the tensile strength and porosity in sintered compacts has been investigated by using electrolytic iron powders. It was shown that the variation in the tensile strength with the porosity (or density) could be expressed separately in three stages, that is, the low density region, the middle density region, and the high density region. The relations of tensile strength and porosity in those three regions can be represented by the following forms.<BR>For the low density region, <BR>S=S'0-k1P (P1<P≤PO)<BR>where S is the tensile strength, P, the porosity, PO, the green porosity, and S'0, k1 and P1, empirical constants. For the middle density region, <BR>S=S'0 exp(-bP) (P2<P≤P1)<BR>where S is the tensile strength, P, the porosity, and SO, b, P1 and P2, empirical constants. For the high density region, <BR>S=(S s+k 2G-1/2)exp(-bP) (P≤P 2)<BR>where S is the tensile strength, G, the grain size, P, the porosity, and S8, K2, b and P2, empirical constants, if the grain size can be represented as a function of porosity, <BR>S=(Ss+k3Pa)exp(-bP) (P≤P2)<BR>where S is the tensile strength, P, the porosity, and S8 k3, a, b and P2, empirical constants.<BR>The empirical constants contained in the above forms were determined by the experimental results. Then, the following forms representing the relations of tensile strength and porosity for the sintered electrolytic iron powder were obtained. When the compressing pressure is 4 t/cm2, for the low density region, <BR>S=132-495P [kg/mm2] (0.23<P≤0.27).<BR>For the middle density region, <BR>S=43.0 exp(-4.4P) [kg/mm2] (0.085<P≤0.23).<BR>For the high density region, <BR>S=(29.5+1.05G-1/2) exp(-4.4P) [kg/mm2] (P≤0.085)<BR>where C is in mm, and<BR>S=(29.5+62.5P0.62) exp(-4.4P) [kg/mm2] (P≤0.085).
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 22 (4), 141-146, 1975
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681285859968
-
- NII論文ID
- 130000815657
-
- NII書誌ID
- AN00222724
-
- COI
- 1:CAS:528:DyaE1cXls1Kqs7k%3D
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 1608518
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可