A tungsten (W) layer whose thickness was tens of micrometers or more was formed by electrical discharge coating using a W electrode which was made from the semi-sintered powder of pure W. The thickness of the W layer was 0.28 times the electrode wear length which was set up as the coating conditions. The density of the W layer was about 12.3×103kg/m3. Many solidified materials whose size was about 10 to 20 micrometers and many voids were observed in the W layer. The Vickers hardness test using the load of 9.8N showed that the hardness of the W layer was 281HV1. The diagonal length of the indentation of the test was several times as large as the solidified material in the W layer. The hardness of the W layer was lower than that of pure W metal.<br>After electron beam irradiating, the densification of the W layer was observed. The thickness of the W layer was contracted from 0.58mm to 0.37mm and the hardness of the layer was improved to 1788HV1.
収録刊行物
-
- 精密工学会誌
-
精密工学会誌 80 (1), 107-111, 2014
公益社団法人 精密工学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204829158272
-
- NII論文ID
- 130003385046
-
- ISSN
- 1882675X
- 09120289
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可