- KUMADA Nobuhiro
- Center for Crystal Science and Technology, University of Yamanashi
-
- RUBEL Mirza Humaun Kabir
- Center for Crystal Science and Technology, University of Yamanashi
-
- MIURA Akira
- Center for Crystal Science and Technology, University of Yamanashi
-
- TAKEI Takahiro
- Center for Crystal Science and Technology, University of Yamanashi
抄録
Spinel-type LiTi2O4 was prepared directly by the reaction of lepidocrocite-type potassium titanate and molten LiCl at 750–850°C in a stream of H2 gas. The Li/Ti ratio in the spinel-type phase prepared at 850°C was 0.54, and the lattice parameter and superconductive critical temperature Tc were a = 8.3935(2) Å and 12.3 K, respectively. The product at 750°C exhibited no superconductive diamagnetism down to 2.5 K, and the product at 800°C showed weak superconductive diamagnetism at 10.5 K. The morphology of the particles prepared at 850°C showed an irregular shape with a particle size of 1–10 µm.
収録刊行物
-
- Journal of the Ceramic Society of Japan
-
Journal of the Ceramic Society of Japan 122 (1424), 307-309, 2014
公益社団法人 日本セラミックス協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680263918336
-
- NII論文ID
- 130003393098
-
- ISSN
- 13486535
- 18820743
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可