New process “SMP” (Slag Minimum Refining Process) which consists of hot metal desiliconization stage in hot metal container and dephosphorization and decarburization stage in LD converter has been studied in order to reduce the consumption of refining fluxes and slag volume yield in conventional LD process.<br>After experimental studies which have been carried out in KR equipment and conventional LD converter to estimate the feasibility of this new process, it becomes clear that hot metal desiliconization treatment can be done with simple equipment by using proper desiliconization agent and flux and its proper adding method.<br>By this new process, CaO consumption for dephosphorization in LD converter and slag volume can be reduced drastically with decreasing Si content in hot metal and that CaO consumption and slag volume required is 18kg/t-s, 42kg/t-s at Si=0.15% for low carbon rimmed steel. As a result, lining life of refractory can be extended and the amount of metal and heat losses can be decreased and it makes the LD refining very stable.<br>Based on the results obtained by the above experiments, a practical equipment of hot metal desiliconization treatment has been installed and came in use in October 1979, and now is in a stable operation.
収録刊行物
-
- Transactions of the Iron and Steel Institute of Japan
-
Transactions of the Iron and Steel Institute of Japan 23 (3), 256-265, 1983
一般社団法人 日本鉄鋼協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206453128064
-
- NII論文ID
- 130003456772
-
- ISSN
- 18811183
- 00211583
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可