Thermodynamic Study of Solid Ni–Ga Alloys by E.M.F. Measurements Using the Solid Electrolyte
-
- Katayama Iwao
- Department of Metallurgy, Faculty of Engineering, Osaka University
-
- Igi Shigeo
- Graduate School, Osaka University
-
- Kozuka Zensaku
- Department of Metallurgy, Faculty of Engineering, Osaka University
書誌事項
- タイトル別名
-
- Thermodynamic Study of Solid Ni–Ga Alloys by E.M.F. Measurements Using the Solid Electrolyte
抄録
E.M.F. of a galvanic cell with the solid electrolyte (ZrO2+CaO) was measured to determine the activities of gallium in the temperature range of 800∼1000°C and the composition range of 5∼58 at% Ga for solid Ni–Ga alloys, and thermodynamic functions were derived from the results. The cells used were as follows;<BR>Pt, Re, Ga, Ga2O3/ZrO2(+CaO)/Fe, FexO, Pt<BR>Pt, Re, (Ni–Ga), Ga2O3/ZrO2(+CaO)/Fe, FexO, Pt<BR>Activities of both components showed large negative deviations from Raoult’s law; Activity change with composition in a nickel-rich α-solid solution and in the α′(Ni3Ga)-phase were small, but very large in the β(NiGa)-phase. Relative integral molar free energies of formation showed minimum values at the stoichiometric composition NiGa. Integral enthalpies and entropies of formation showed relatively large negative values.
収録刊行物
-
- Transactions of the Japan Institute of Metals
-
Transactions of the Japan Institute of Metals 15 (6), 447-453, 1974
社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205118146432
-
- NII論文ID
- 130003485328
-
- ISSN
- 24324701
- 00214434
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可