- Izumi Osamu
- The Research Institute for Iron, Steel and Other Metals, Tohoku University
-
- Takasugi Takayuki
- The Research Institute for Iron, Steel and Other Metals, Tohoku University
抄録
Tensile tests were performed on bicrystals and corresponding component crystals of Al-3%Cu heat-treated to different stages of ageing, that is, those of supersaturation, intermediate phase formation and stable phase precipitation. The stress-strain curves were analysed from the point of view of the effect of ageing and crystal orientation on deformation. The following results were obtained: (1) The strength of a supersaturated solid solution is determined by the compatibility condition and the dislocation pile-up mechanism at a grain boundary. (2) No simple relationship was established for both intermediate phase formation and stable phase precipitation. (3) The “grain boundary strength” Δσε of the supersaturated solid solution shows a parabolic relation against strain. (4) The “grain boundary strength” for the intermediate phase initially shows a parabolic strain dependence, but decreases to a negative value as deformation proceeds. (5) The “grain boundary strength” for the stable precipitation shows a parabolic strain dependence similar to that at the supersaturation stage.
収録刊行物
-
- Transactions of the Japan Institute of Metals
-
Transactions of the Japan Institute of Metals 16 (7), 397-408, 1975
社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205119154304
-
- NII論文ID
- 130003485391
-
- COI
- 1:CAS:528:DyaE28XptlyqtA%3D%3D
-
- ISSN
- 24324701
- 00214434
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可