- Fujiwara Syoji
- Department of Metal Science and Technology, Faculty of Engineering, Kyoto University
-
- Shiraga Tetuo
- Graduate School, Kyoto University
-
- Tamura Imao
- Department of Metal Science and Technology, Faculty of Engineering, Kyoto University
書誌事項
- タイトル別名
-
- Precipitation Behavior in Fe–Mn–Cu Austenitic Alloys
抄録
The precipitation behavior in Fe–Mn–Cu austenitic alloys was studied by means of the hardness test, electric resistivity measurement, Mössbauer effect measurement, and optical and transmission electron microscopy. The main results obtained are as follows: In Fe–Mn–3Cu, Fe–Mn–5Cu and Fe–Mn–7Cu alloys, an age-hardening phenomenon was observed and the degree of hardening, became remarkable with increase in Cu content. In this alloy system, a two-phase decomposition was expected to occur and it was considered to be based on a miscibility gap in the Fe0.5 Mn0.5–Cu quasi-binary system. Namely, it was suggested that these Fe–Mn–Cu alloys were decomposed into a Fe–Mn rich (Cu-poor) phase and a Cu-rich phase. By means of splat-quenching from the liquid state an austenitic single phase of Fe–Mn–40Cu alloy was obtained and the two-phase decomposition was also expected to occur in this alloy.
収録刊行物
-
- Transactions of the Japan Institute of Metals
-
Transactions of the Japan Institute of Metals 17 (5), 294-302, 1976
社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282680095536128
-
- NII論文ID
- 130003485484
-
- COI
- 1:CAS:528:DyaE28Xls1Cgtr8%3D
-
- ISSN
- 24324701
- 00214434
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可