- Tagashira Kohsuke
- Department of Mechanical Engineering, Muroran Institute of Technology
-
- Kobayashi Masaharu
- Asahikawa Technical College
-
- Nakae Hitoshi
- Department of Precision Engineering, Faculty of Engineering, Hokkaido University
-
- Hoshi Koichi
- Asahikawa Technical College
抄録
The textures of Fe-3.25%Si alloys by low speed cutting (76 mm/min) were determined by X-ray diffractometion and optical gonio microscopy. In the orthogonal cutting of single crystals with various orientations, a few preferred orientations such as (011)[100] and (‾132)[201] were observed in the deformed regions from the cutting surfaces to a depth of about 50 μm. Conventional plane cutting of polycrystalline specimens of nearly random texture with 3 different grain sizes formed a texture with a major (011)[100] orientation and minor (111)[11\bar2] and (0\bar12)[\bar421] ones. The intensity of the (011)[100] main component increased and its dispersion decreased with the average grain size. Further, the main component in the cutting surfaces of the polycrystalline specimens became obvious in two-pass cutting.
収録刊行物
-
- Transactions of the Japan Institute of Metals
-
Transactions of the Japan Institute of Metals 19 (11), 617-624, 1978
社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282680094487808
-
- NII論文ID
- 130003485619
-
- COI
- 1:CAS:528:DyaE1MXhsFGhtbs%3D
-
- ISSN
- 24324701
- 00214434
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可