- Suto Hajime
- Department of Materials Science, Faculty of Engineering, Tohoku University
-
- Sato Shinji
- Department of Materials Science, Faculty of Engineering, Tohoku University
書誌事項
- タイトル別名
-
- Grain Boundary Internal Friction of Ni and Ni–B Alloys
抄録
In order to investigate the solid solubility of B in Ni as a function of grain size, the high temperature internal friction of pure Ni and Ni–B alloys containing 0.0035, 0.0068 and 0.010 wt% B has been measured with particular attention to the grain boundary damping peaks. The electrical resistivity was also measured to determine the solubility. The results obtained are summarized as follows:<BR>(1) The solubility of B in single crystal Ni is given by C(at%)=0.59exp(−H⁄RT), H=65.6 kJ/mol.<BR>(2) The apparent solubility of B in polycrystalline Ni increases remarkably with decreasing grain size.<BR>(3) On the Q−1−1⁄T curves of pure Ni, there are two peaks of grain boundary damping at about 470°C and about 670°C. By addition of 0.0035 wt% B, only one peak can be observed. The peak temperature of every Ni–B alloy used is about 550°C and its activation energy is about 330 kJ/mol.
収録刊行物
-
- Transactions of the Japan Institute of Metals
-
Transactions of the Japan Institute of Metals 21 (2), 83-88, 1980
社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282680094110336
-
- NII論文ID
- 130003485819
-
- COI
- 1:CAS:528:DyaL3cXktlSnsLs%3D
-
- ISSN
- 24324701
- 00214434
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可