New Type of M<SUB>23</SUB>C<SUB>6</SUB> Carbide Precipitation in an Austenitic Stainless Steel Containing Niobium
-
- Terao Nobuzo
- Laboratory of Physical Metallurgy, Catholic University of Louvain
-
- Sasmal Bimalendu
- Laboratory of Physical Metallurgy, Catholic University of Louvain
抄録
An electron microscopic study has been made of precipitation in an austenitic stainless steel, 16Cr–16Ni–0.8Nb–1.8Mo–0.06C. Attention has been focused on structural changes which take place during long ageing treatments, extended up to 14.4 Ms (4000 h). In addition to the well-known chromium rich M23C6 carbides, which appear, together with NbC, from the beginning of the precipitation treatment at 1073 K, a new plate-like morphology of M23C6 carbide precipitation was observed after long ageing treatments. These M23C6 carbide plates were formed on {110} planes in regions near pre-existing undissolved NbC particles and their edges were bounded by {111} planes of the fcc alloy matrix. It is suggested that this unexpected process might be favoured by the stresses produced around the undissolved NbC particles.
収録刊行物
-
- Transactions of the Japan Institute of Metals
-
Transactions of the Japan Institute of Metals 22 (6), 379-384, 1981
社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205117734400
-
- NII論文ID
- 130003485909
-
- COI
- 1:CAS:528:DyaL3MXkvVOrurY%3D
-
- ISSN
- 24324701
- 00214434
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可