Morphological Change and Recovery during Tempering of Ni<SUB>40</SUB>Zn<SUB>50</SUB>Cu<SUB>10</SUB> Martensite
-
- Murakami Yuichiro
- Department of Chemistry, Faculty of Science, Kyoto University
-
- Kachi Sukeji
- Department of Chemistry, Faculty of Science, Kyoto University
-
- Nakanishi Norihiko
- Department of Chemistry, Faculty of Science, Konan University
抄録
The morphological change during tempering the Ni40Zn50Cu10 martensite (L10 structure) was studied by means of optical and electron microscopy. The morphology of the L10 phase changed from the martensitic structure to the massive one during tempering at 823 K. At the early stage of tempering, new interface boundaries appeared and polygonal grains were formed in a martensite plate due to the polygonization. During further tempering, many subgrains were formed. The volume fraction of the twin decreased gradually in a polygonal grain. At the late stage of tempering, large massive grains appeared and a few thin plates of (111)L1<SUB>0</SUB> twins existed as growth faults inside them. The surface relief of the L10 martensite disappeared gradually with the growth process of the massive grains. These phonomena were discussed briefly in relation to the recovery and the recrystallization.
収録刊行物
-
- Transactions of the Japan Institute of Metals
-
Transactions of the Japan Institute of Metals 25 (8), 538-544, 1984
社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680095734784
-
- NII論文ID
- 130003486158
-
- COI
- 1:CAS:528:DyaL2cXmtlChtrs%3D
-
- ISSN
- 24324701
- 00214434
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可