Shear Band Formation in Al-2mass%Cu Single Crystals Containing ϑ Precipitates

• Morii K.

  College of Engineering, University of Osaka Prefecture

• Terada H.

  Graduate Student, University of Osaka Prefecture

• Nakayama Y.

  College of Engineering, University of Osaka Prefecture

書誌事項

タイトル別名

• Shear Band Formation in Al-2mass%Cu Single Crystals Containing ϑ Precipitates

抄録

The effect of θ precipitates and deformation at elevated temperatures on the shear band formation has been investigated in rolled single crystals of an Al-2%Cu alloy based on observations of slip bands and dislocation structures. Irrespective of heat treatments to give either a nominal solid solution or θ precipitates, shear bands were not formed in (011)[\bar100] crystals but in (211)[\bar111] crystals during rolling at room temperature. Increase in the temperature up to 473 K resulted in rather homogeneous slip and developed no shear bands even in the (211)[\bar111] crystals. A simple correlation between the shear band formation and dislocation structures was found; the shear bands occurred in the crystals in which aligned micro-bands (layered dislocation walls) evolved.

収録刊行物

• Transactions of the Japan Institute of Metals

  Transactions of the Japan Institute of Metals 27 (10), 769-774, 1986

  社団法人 日本金属学会

キーワード

• shear bands
• localized slip
• aluminum-alloy
• θ-precipitates
• rolling deformation

詳細情報

• CRID: 1390001205117855744
• NII論文ID: 130003486256
• DOI: 10.2320/matertrans1960.27.769
• COI: 1:CAS:528:DyaL2sXot1Oj
• ISSN: 24324701
• ISSN: 00214434
• Web Site: https://www.jstage.jst.go.jp/article/matertrans1960/27/10/27_10_769/_pdf
• 本文言語コード: en
• データソース種別:
  • JaLC
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可