スリット型による軟鋼熔接棒の亀裂性試験
-
- 安藤 精一
- 鉄道技術研究所
書誌事項
- タイトル別名
-
- Crack Test of Mild Steel Electrode with Slit Type Specimens
- In welding of rimmed steel
- Rimmed鋼熔接の場合
抄録
About 40 commercial mild steel electrodes of different types (all except three passing the mechanical test specified by AWS or JIS) were used for welding slit-type crack test specimens prepared of several grades of rimmed steels and the crack development in them has been observed with the folio wing results:<BR>1) Apparently there is no relationship between the mechanical properties of all deposit metals and crack tendency.<BR>2) In the room-tempreture welding of steel plates with ordinary composition, with some exceptions there is a very low incidence of crack development whatever electrode may be used.<BR>3) Considerable variance in crack tendency is observed depending upon the grade of electrode, with high-S (for instance, 0.046%) steel plates to be welded at room temperature.<BR>4) Crack tendency of steel plates with usual components when they are welded at low temperature, say 0°C, follows the same pattern as. that of high-S steel but is not so marked as the latter.<BR>5) Deoxidation of. deposit metal seems to have something to do with crack tendency. Effect of deoxidation is great when high-S steels are welded or welding is done at low temperature. Every type of electrode with high Si/Mn deposit metal, excepting low hydrogen type, possesses high crack tendency.<BR>Low hydrogen type is most stable to cracks, followed by the ilmenite type, containing a conside-rable amount of Mn and low Si/Mn, with fairly good stability.
収録刊行物
-
- 溶接学会誌
-
溶接学会誌 22 (8), 258-265, 1953
一般社団法人 溶接学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206500490240
-
- NII論文ID
- 130003762568
-
- ISSN
- 18837204
- 00214787
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可