溶着鋼の遷移温度

• 大谷 碧

  鉄道技術研究所

• 岡田 寛

  東洋電極工業株式会社

書誌事項

タイトル別名

• Transition Temperature of Deposited Steel

抄録

By varying the coating composition of electrodes, the properties of deposited metals were changed in series with regard to their elements and degree of deoxidation. Their ordinary mechanical properties were kept as constant as possible. The impact test results showed that the degree of deoxidation considerably affected the transition temperature. It was suggested that theexperimental formula by M. Williams, which showed the relation between max. T_r15 (°C) and chemical composition (%) of steel should be supplemented by the term, plus 790 FeO.<BR>The detrimental effects of P was also pronounced in deposited steel.

収録刊行物

• 溶接学会誌

  溶接学会誌 23 (5-6), 104-110, 1954

  一般社団法人 溶接学会

キーワード

• Metals and Alloys
• Surfaces, Coatings and Films
• Mechanical Engineering
• Mechanics of Materials

詳細情報

• CRID: 1390001206501145856
• NII論文ID: 130003762573
• DOI: 10.2207/qjjws1943.23.104
• ISSN: 18837204
• ISSN: 00214787
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可