超高張力鋼の溶接性に関する研究(第1報)
書誌事項
- タイトル別名
-
- A Study on Weldability of a New Ultra-High-Tensile-Strength Steel (Report 1)
抄録
A new ultra-high-tensile-strength steel was developed by addition of proper amount of AlN, which is known as IN-treatment, to a commerical 80 kg/mm2 high tensile strength steel. The development was carried out as a joint work with the YAWATA IRON & STEEL CO., LTD, Prior to use for steel structure or pressure vesseles, various weldability tests were undertaken, and it has been established that the ultra-high-tensile-strength steel has completely satisfactory weldability. After the tests, authors reached following conclusions.<BR>1. Weld-joint properties are satisfactory and quite comparable to those of base metal, when optimum welding condition is applied.<BR>2. To increase the ductility in free bend specimen of weld-joint, it is necessary to keep weld-heat-input to a range of 20, 000-32, 000 joule/cm.<BR>3. Preheating to 120°C or higher is quite effective to avoud cracks in 25 mm thick weld-joint.<BR>4. Some deterioration is observed in weld-heat-affected-zone in V-notch charpy impact test for weldment. Authors have pointed out the need for further investigation of the phenomenon.
収録刊行物
-
- 溶接学会誌
-
溶接学会誌 36 (7), 766-773, 1967
一般社団法人 溶接学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206501856640
-
- NII論文ID
- 130003763028
-
- ISSN
- 18837204
- 00214787
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可