溶接部熱・拘束応力・ひずみサイクル試験装置の開発とその応用例について

• 稲垣 道夫

  金属材料技術研究所

• 西川 淳

  金属材料技術研究所

• 頴娃 一夫

  金属材料技術研究所

• 峰松 裕行

  富士電波工機株式会社

• 小管 信吾

  富士電波工機株式会社

• 中村 治方

  新日本製鉄株式会社

書誌事項

タイトル別名

• Development and Its Application of Weld Thermal-Restraint Stress and Strain-Cycles Simulator

抄録

A weld thermal-restraint stress and strain-cycles simulator, briefly "Thermal Restraint Simulator; Thermorestor", which enables us to simulate various phenomena caused by welding, and to analyze separately the effects of each factor such as thermal cycles, restraint stress cycles, strain cycles and atmosphere upon materials, has been developed.<BR>It is confirmed that this apparatus can be applied to making clear weld cracking phenomena, to evaluation of weldability of base metal, to selection of welding materials, to establishment of welding procedure and so on.<BR>Examples of standard programs and their application tests for investigation of welding phenomena with this apparatus are as follows:<BR>1) The program of a rigid restraint control during synthetic weld thermal cycles can make clear the weld hot crack sensitivity in the heat-affected zone of base metals.<BR>2) By the program of enforced strain control during synthetic weld thermal cycles they can investigate the hot crack sensitivity and the propagation characteristics of micro-cracks of base metlas or weld metals, and me program is useful for selection of base metals or welding materials.<BR>3) The program of a constant strain control during cooling of a notched specimen charged with hydrogen at a high temperature can make cleur the phenomena of delayed cracking due to hydrogen, and is very useful for the evaluation of cold crack sensitivity during welding and dealyed cracking characteristic during operation.<BR>4) The programs of various controlled strain or stress during weld post-heat treatment can make clear stress relaxation and anneal cracking phenomena, and are used for decision of the conditions of stress relief heat treatment and the evaluation of anneal crack sensitivity of base metals.

収録刊行物

• 溶接学会誌

  溶接学会誌 41 (11), 1315-1329, 1972

  一般社団法人 溶接学会

キーワード

• Metals and Alloys
• Surfaces, Coatings and Films
• Mechanical Engineering
• Mechanics of Materials

詳細情報

• CRID: 1390282681479628544
• NII論文ID: 130003763198
• DOI: 10.2207/qjjws1943.41.1315
• ISSN: 18837204
• ISSN: 00214787
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可