不溶着切欠付3点曲げ(BNP)試験によるボンドじん性の評価
書誌事項
- タイトル別名
-
- Evaluation of Fracture Toughness of Coarse Grained HAZ by Means of Three Points Bend Specimen with Notch of Poor Penetration
抄録
A new test method has been proposed to evaluate bond's fracture toughness (δc) easily. Three points bend (BNP) specimens were extracted from welded test blocks with notch of poor penetration.<BR>The tip of the notch in BNP specimen was located on a fusion line in modified-Vee joint. Three points bend tests have been made on weldments of three kinds of structural steels, and fracture toughness of bond has been measured over a wide temperature range using BNP test specimens. Results can be summarrized as follows;<BR>1. To estimate the bond's toughness exactly, notch tip must be laid in the coarse grained HAZ zone, but it is wearisome to machine such notch.<BR>2. The notch tip of the BNP specimen is precisely on fusion line, and it is easy to prepare BNP specimen.<BR>3. Bond's toughness of BNP specimen largely depends on angular distortion of joint.<BR>4. Temperature dependenceiof bond's toughness can be easily estimated with safety, by using BNP specimen welded under high bending constraint to prevent the occurence of angular distortion during welding.
収録刊行物
-
- 溶接学会誌
-
溶接学会誌 48 (5), 309-314, 1979
一般社団法人 溶接学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681479431296
-
- NII論文ID
- 130003763500
-
- ISSN
- 18837204
- 00214787
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可