- Study on the Electron Beam Welding of 50kgf/mm<SUP>2</SUP> Class Nodular Cast Iron
- ポロシテイにおよぼす溶接条件の影響
抄録
This report describes the effect of welding conditions on porosities for electron beam welding of 50 Kgf/mm2 class nodular cast iron (6, 12, 18 mm thickness) with SUS304 (0.5 mm thickness) as insert metal.<BR>The results obtained in this experimental investigation are summarized as follows;<BR>(1) Amount of porosities of the fusion zone remarkably decreases by pretreatment annealing (950°C ×5 hr).<BR>(2) For the range of ab value from 0.7 to 0.9, well type beads are formed and no crack is observed.<BR>(3) For the range of ab value more than unity, wedge type beads are formed and weld cracks occurred and porosities increased.<BR>(4) Amount of porosities has tendency to decrease as beam current increase and to increase as welding speed increase.<BR>(5) For base metal of 6, 12 mm thickness, amount of porosities is remarkably decreased by 1 pass weld and for 18 mm thickness remarkably decreased by 2 passes weld.<BR>(6) Under optimum welding conditions, sufficient strength of the welded joint can be obtained.
収録刊行物
-
- 溶接学会誌
-
溶接学会誌 51 (9), 748-754, 1982
一般社団法人 溶接学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681477031040
-
- NII論文ID
- 130003763655
-
- COI
- 1:CAS:528:DyaL3sXjvVGhuw%3D%3D
-
- ISSN
- 18837204
- 00214787
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可