The weldability of Inconel 713C casted alloy and Inconel 718 forged alloy for high tmeperature components was investigated as a dissimilar metal joint by electron beam welding. As a result, fine Equation cracks in HAZ of the joint were detected by microscopic examination. This type of crack was very difficult to be prevented only by changing EB welding parameters. Then, it was experimentally found that hot isostatic pressing as a thermomechanical process could completely healed such fine cracks. And tensile strength at elevated temperature and creep rupture stress of HIPed joints after EB welding were not less than those of Inocnel 718 alloy.

収録刊行物

• 溶接学会論文集

  溶接学会論文集 1 (2), 181-188, 1983

  一般社団法人 溶接学会

キーワード

• Metals and Alloys
• Surfaces, Coatings and Films
• Mechanical Engineering
• Mechanics of Materials

詳細情報

• CRID: 1390282679700186880
• NII論文ID: 130003764363
• DOI: 10.2207/qjjws.1.181
• ISSN: 24348252
• ISSN: 02884771
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可