改良型HP系耐熱鋳鋼の経年使用材の補修溶接割れ 1 小型スポットバレストレイン試験による高温割れ感受性評価
書誌事項
- タイトル別名
-
- Evaluation of Hot-Cracking Susceptibility by Miniature Spot-Varestraint Testing. Repair Weld Cracking of Long Term Exposed HP-Modified Heat-Resisting Cast Alloys. (Report 1).
- Repair Weld Cracking of Long Term Exposed HP-Modified Heat-Resisting Cast Alloys (Report 1)
- 改良型HP系耐熱鋳鋼の経年使用材の補修溶接割れ(第1報)
抄録
The hot cracking susceptibilities of HP-modified heat-resisting cast alloys exposed at the elevated temperature for the long term were evaluated by the miniature spot-Varestraint testing. The as-cast, aging and/or used (service exposed) specimens of seven types of the HP-modified alloys were employed for the spot-Varestraint testing. Ductility-dip cracking as well as liquation cracking was occurred in HAZ of each specimen after the spot-Varestraint testing. The ductility-dip cracking susceptibilities of alloys except for HP43AZ much increased in aged and used conditions compared with as-cast condition, while the liquation cracking susceptibilities did not change so much during long term aging. The ductility-dip cracking susceptibility of HP43AZ containing zirconium was remarkably restrained even in used condition. It was deduced that the improvement in the ductility-dip cracking susceptibility of HP43AZ was attributed to reducing the occupied ratio of microconstituents on cellular dendrite boundary by the zirconium addition which possessed refinement effect of dendritic cell.
収録刊行物
-
- 溶接学会論文集
-
溶接学会論文集 18 (3), 438-448, 2000
一般社団法人 溶接学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679698887296
-
- NII論文ID
- 130003764643
-
- ISSN
- 24348252
- 02884771
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可