非鉄金属のプラズマイオン窒化法による表面改質 第3報 ホローカソード放電を利用した高速プラズマイオン窒化法の検討
書誌事項
- タイトル別名
-
- Studies of surface modification of nonferrous metals by means of plasma ion nitriding (PIN) process (report 3). Rapid plasma ion nitriding process by means of hollow cathode glow discharge.
- Studies of Surface Modification of Nonferrous metals by means of Plasma Ion Nitriding (PIN) Process (Report 3)
- 非鉄金属のプラズマイオン窒化法による表面改質(第3報)
抄録
The feasibility of a rapid plasma ion nitriding process assisted by hollow cathode discharge has been examined for austenitic stainless steel (SUS304), ferritic stainless steel (SUS340) and Ni base heat resistant alloys (Inconel 625 and Udimet 500).<BR>Hollow cathode discharge was easily realized by arranging two specimens on a cathode plate, so that their treating faces were set parallel at an optimum distance, which was different depending on the pressure of N2+H2 mixed gas as 3 mm for 800 and 1330Pa, 5 mm for 270Pa or 15 mm for 80Pa. At these optimum conditions, the nitriding speed was increased to about 2 times as fast as that for a conventional plasma ion nitriding process at the same nitriding temperature and time without any decrease in the hardness of nitrided layer. This increase in nitriding speed was considered to be due to the high ionization rate of hollow cathode discharge in comparison with conventional glow discharge.
収録刊行物
-
- 溶接学会論文集
-
溶接学会論文集 8 (2), 267-272, 1990
一般社団法人 溶接学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204723113856
-
- NII論文ID
- 130003764887
-
- ISSN
- 24348252
- 02884771
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可