Impregnation of Calcium Chloride into Alumina Thin Film Prepared by Oxalic Acid Anodizing

DOI Web Site Web Site 被引用文献2件 参考文献13件
  • Suwa Yuji
    Graduate School of Natural Science and Technology, Kanazawa University
  • Kumita Mikio
    College of Science and Engineering, School of Natural System, Kanazawa University
  • Komori Hiroaki
    Graduate School of Natural Science and Technology, Kanazawa University
  • Kodama Akio
    College of Science and Engineering, School of Mechanical Engineering, Kanazawa University
  • Otani Yoshio
    College of Science and Engineering, School of Natural System, Kanazawa University

この論文をさがす

抄録

In the present study, a calcium chloride-oxalic acid anodized alumina composite was proposed as a sorbent of water vapor for the application to adsorption chiller. CaCl2-anodic alumina composite sorbents were prepared by anodic oxidation of an aluminum plate in an oxalic acid bath, following the widening of pores in anodic oxide films with a sulfuric acid solution and the impregnation of saturated aqueous solution of CaCl2 into the pores at a reduced pressure. As a result, the alumina films prepared in an oxalic acid bath had numerous large pores, and their porosities were significantly larger than those of sulfuric acid-anodized alumina films. The amounts of CaCl2 impregnated into the alumina films were a function of the apparent densities of the films, and the maximum CaCl2 content was 39.7 wt%. The CaCl2-anodic alumina composites were capable of sorbing water vapor even in the relative pressure range below 0.3. With higher doses of CaCl2 contained by the alumina film, a larger amount of water vapor was sorbed by the composite. Furthermore, the CaCl2-oxalic acid anodized alumina composite showed a fast water sorption rate like commercial silica-gel particles.