- Effect of solidification conditions on microstructures of unidirectionally solidified AZ91C alloy.
- MC2 マグネシウム ゴウキン ノ ソシキ ニ オヨボス ギョウコ ジョウケン
この論文をさがす
抄録
AZ91C magnesium alloys were unidirectionally solidified at various liquid cooling rates (V LC), average cooling rates in solidification range (V SC), temperature gradients (G), moving velocities of solid-liquid interface (R) and G/R ratios. Equiaxed dendrite structure was obtained by the superheating of molten metal. Dendrite cell size decreases exponentially with increasing liquid cooling rate. With increasing average cooling rate and with decreasing temperature gradient, the amount of eutectic compounds increases and it extends at triple junctions of cell boundaries and individual cell boundaies. In AZ91C-T6 alloy, the eutectic compounds dissolve by solution heat treatment. Discontinuous precipitates along cell boundaries were observed by optical microscopy and their width decreases with increasing liquid cooling rate.
収録刊行物
-
- 軽金属
-
軽金属 37 (11), 714-720, 1987
一般社団法人 軽金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206339664512
-
- NII論文ID
- 130004075754
- 10004011275
-
- NII書誌ID
- AN00069773
-
- COI
- 1:CAS:528:DyaL1cXhtlGqtbc%3D
-
- ISSN
- 18808018
- 04515994
- http://id.crossref.org/issn/04515994
-
- NDL書誌ID
- 3157754
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可