- Effect of heat treatment on the mechanical properties of AC4CH casting alloy.
- AC4CH アルミニウム ゴウキン イモノ ノ キカイテキ セイシツ ニ オヨ
この論文をさがす
抄録
Age hardening process of the AC4CH casting alloy solution treated at 843K was investigated mainly in view of aging temperatures. About 5 to 10% improvement of the tensile properties were obtained for the aging treatment at 418K for longer aging time as compared with those of the alloys heat treated with the conventional conditions. The percent elongation to the fracture and the absorbed energy, however, were not effectively improved. Reasonable correspondence between 0.2% proof stress and the specific resistance ratio were obtained. The proof stress was higher for the specimens aged at lower temperatures, although the resistance ratios were identical. The calculated m values of the Johnson-Mehl's equation for the precipitating particles were different for higher and lower temperatures, suggesting that the growth behavior of the particles was elassified into two types.
収録刊行物
-
- 軽金属
-
軽金属 43 (11), 612-617, 1993
一般社団法人 軽金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206335670912
-
- NII論文ID
- 130004075928
- 10003903668
- 10003033430
-
- NII書誌ID
- AN00069773
-
- COI
- 1:CAS:528:DyaK2cXhtFenu74%3D
-
- ISSN
- 18808018
- 04515994
- http://id.crossref.org/issn/04515994
-
- NDL書誌ID
- 3853529
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可