粉末液相鍛造法によるＡｌ２Ｏ３あるいはＳｉＣ粒子／６０６１アルミニウム合金複合材料の作製とその機械的性質

DOI Web Site 被引用文献3件

書誌事項

タイトル別名
  • Application of powder liquid forging technique to fabrication of Al2O3 or SiC particle/6061 Aluminum alloy metal matrix composites and their mechanical properties.
  • フンマツ エキソウ タンゾウホウ ニ ヨル Al2O3 アルイハ SiC リュ

この論文をさがす

抄録

The powder-liquid-forging (PLF) process was employed to make SiC or Al2O3 particle/6061 aluminum alloy metal- matrix-composite (MMC). Since the aluminum alloy powder is enveloped by oxide layer, usual sintering is difficult. It becomes, however, possible to break the oxide film to sinter, when a powder compact is pressed above the melting point. This unique PLF technique has been found to be applicable to produce MMCs containing up to 30% of the reinforcement with high density. The Young's modulus and hardness of solution treated MMCs are monotoneously increased with an increase in the volume fraction of reinforcement of either SiC or Al2O3. The age-hardening decreases drastically in Al2O3/6061 MMC but a little in SiC/6061 one. This is because the spinel (MgAl2O4) formes in Al2O3/6061 MMCs during the PLF process, i. e., the loss of magnesium in the 6061 matrix is considered to lower age-hardening. Even in a SiC/6061 MMC in which such a reaction at the interface was not detected, the precipitation by the aging is suspected to occur very inhomogeneously. The tensile strength at room temperature is increased by adding the rein forcement particles. However, the tensile strengths of MMCs above 450K become to be approximately the same as those of the 6061 alloy prepared by the conventional ingot metallurgy.

収録刊行物

  • 軽金属

    軽金属 43 (4), 213-218, 1993

    一般社団法人 軽金属学会

被引用文献 (3)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ