過熱処理したＭｇ‐Ａｌ合金の鋳造組織と結晶粒微細化

DOI Web Site 被引用文献3件

書誌事項

タイトル別名
  • Cast structures and grain refinement of superheat-treated Mg-Al alloy.
  • カネツ ショリシタ Mg Al ゴウキン ノ チュウゾウ ソシキ ト ケッショ

この論文をさがす

抄録

In order to understand the mechanisms of grain refinement of a superheat-treated magnesium alloy, pure magnesium samples containing 0 to 10at%Al were heated at 900°C and held for 1800s. The samples were then cooled at a constant rate and cast into a metallic mold at 660 or 680°C. Samples were melted ln the graphite, cast iron, and magnesla crucibles to clarify the influences of impurity elements in the crucible on the grain size. Metallographic examinations were performed to measure the grain size of solidified structures. An electron probe micro analyzer was used to find the foreign particles for heterogeneous nucleation in the fine grains. The grain refinement of superheat-treated Mg-Al alloys depends on aluminum content. The finest grain size was obtained in the Mg-6at%Al alloy. The grain size became coarser as the aluminum content increased or decreased from 6%. The molten magnesium alloy attacked the iron and magnesia crucibles, so Fe and Si contents of samples increased. However, no foreign particles such as metallic compounds which occur in heterogeneous nucleation were observed in any grain.

収録刊行物

  • 軽金属

    軽金属 44 (8), 427-432, 1994

    一般社団法人 軽金属学会

被引用文献 (3)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ