- 金子 純一
- 金属材料技術研究所 日本大学生産工学部
書誌事項
- タイトル別名
-
- Age-hardening behavior of thermomechanically treated Al-Mg-Si alloys
- カコウ ネツ ショリシタ Al Mg Si ゴウキン ノ ジコウ コウカ キョ
この論文をさがす
抄録
Age-hardening behavior in final aging of TMT, in which plastic deformation is applied after pre-aging but prior to final aging, has been studied. The hardening behavior in this type of TMT is in general correlation with that in two-step aging. The strength of TMT materials increases with rising pre-aging temperature. The amount of age-hardening is degreased by plastic deformation prior to final aging due to heterogeneous precipitation on dislocations. Pre-aging prior to plastic deformation is more effective in increasing the maximum hardness in final aging than in two-step aging. This is attributed to retardation of heterogeneous precipitation on dislocations. In commercial 6061 alloy, the strength can be increased by TMT as high as 10% in contrast to the high purity alloy of the same Mg2Si content. Such differences in two-step aging and TMT behaviors between high purity and commercial alloys are attributed to metallographic heterogeneity existing in the latter.
収録刊行物
-
- 軽金属
-
軽金属 27 (8), 384-390, 1977
一般社団法人 軽金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206340943616
-
- NII論文ID
- 130004207941
- 10003795699
-
- NII書誌ID
- AN00069773
-
- COI
- 1:CAS:528:DyaE1MXkt1CnsA%3D%3D
-
- ISSN
- 18808018
- 04515994
-
- NDL書誌ID
- 1838680
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可