Ａｌ‐ＳｉおよびＡｌ‐Ｇｅ合金の凝固現象の直接観察

DOI Web Site 被引用文献4件

書誌事項

タイトル別名
  • In-situ observation of solidification phenomena of Al-Si and Al-Ge alloys.
  • Al Si オヨビ Al Ge ゴウキン ノ ギョウコ ゲンショウ ノ チョク

この論文をさがす

抄録

In order to understand the solidification mechanism of Al-Si and Al-Ge alloys, in-situ observation of the solidication phenomena on the molten surface has been carried out during unidirectional solidification. In hypoeutectic alloy containing 8 to 10mass% Si or 46 to 51mass% Ge, eutectic solidification starts at the cooling end and then unidirectionally proceeds independently of the primary crystal of α aluminum dendrites which exists in the eutectic melt. In eutectic compositions containing 11.7mass% Si or 53mass% Ge, only unidirectional solidification of eutectic occurs. In this case, eutectic Si or Ge crystals are always observed to precede at the competitive growth with eutectic aluminum. These phenomena show that the silicon and germanium are the leading phases of the eutectic in these alloys. In hypereutectic composition containing 14 to 18mass% Si or 55 to 60mass% Ge, eutectic solidification starts on primary crystals of angular silicon or germanium and then spreads radially in the melt. These results are consistant with those previously obtained on Al-Cu, Al-Ni, Zn-Al and Sn-Zn eutectic alloys.

収録刊行物

  • 軽金属

    軽金属 38 (2), 96-101, 1988

    一般社団法人 軽金属学会

被引用文献 (4)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ