書誌事項
- タイトル別名
-
- Properties of alumina particles dispersed aluminum alloy composites fabricated by powder liquid forming technique.
- フンマツ エキソウ セイケイホウ デ サクセイシタ アルミナ リュウシ ブンサ
この論文をさがす
抄録
Aluminum alloy matrix composites containing Al2O3 particles were fabricated by powder liquid forming technique. Tensile properties of composites depended on the size of alumina particles, and tensile strength showed 550MPa for 30 wt%Al2O3 (d=0.5μm)/6061 aluminum alloy composites. Aging sequence of composites was accelerated by the presence of alumina particles compaired with the matrix alloy. Spinel compounds (MgAl2O4) were detected in the Al2 O3/6061 aluminum alloy composites heated at high temperature for a long period. Thermal expansion coefficients of 6061 and AC8A alloy composites containing 30wt%Al2O3 particles respectively were reduced about 20% compaired with the matrix alloys.
収録刊行物
-
- 軽金属
-
軽金属 39 (4), 262-268, 1989
一般社団法人 軽金属学会
- Tweet
詳細情報
-
- CRID
- 1390282681316801408
-
- NII論文ID
- 130004208883
- 10003342068
-
- NII書誌ID
- AN00069773
-
- COI
- 1:CAS:528:DyaL1MXltVWms7g%3D
-
- ISSN
- 18808018
- 04515994
- http://id.crossref.org/issn/04515994
-
- NDL書誌ID
- 3235750
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可